6
layers
≥1050
MPa at the cervical (avg.)
57%
translucency at the incisal
1500 °C
recommended sintering
Why 3D PLUS ML
Strength at the base, light at the edge.
Six layers grade both colour and material: a stronger, more chromatic cervical for connectors and margins, a more translucent incisal for natural aesthetics, with no dyeing step.
6-layer colour
A natural shade gradient across six layers, built into the disc.
Translucency 43 → 57%
Translucency increases towards the incisal edge for a lifelike result.
Strength 700 → 1050 MPa
Strength builds towards the cervical, for crowns and bridges up to 3 units.
Physical characteristics
| Sintered density | 6.07 ± 0.03 g/cm³ |
|---|---|
| Bending strength | ≥700–1050 MPa (avg.) |
| Transmittance | 43–57% |
| Hardness | 1200 HV |
| Sintering temperature | 1500 °C (recommended) |
CervicalIncisal
Drag along the disc to explore each layer
Cervical
Layer 6
Yttria
4Y
Translucency
43%
Flexural strength
≥1050 MPa
Layer by layer
| Layer | Thickness | Translucency | Yttria | Strength |
|---|---|---|---|---|
| Layer 1 | 20% | 57% | 5Y | ≥700 MPa |
| Layer 2 | 15% | 55% | 4Y·5Y | ≥760 MPa |
| Layer 3 | 15% | 53% | 4Y·5Y | ≥830 MPa |
| Layer 4 | 15% | 50% | 4Y·5Y | ≥890 MPa |
| Layer 5 | 15% | 47% | 4Y·5Y | ≥960 MPa |
| Layer 6 | 20% | 43% | 4Y | ≥1050 MPa |
Indications
From inlay to 3-unit bridge.
Crown
Inlay
Onlay
Bridges up to 3 units
Anterior
Shade range
20 shades.
The full VITA classical range A1–D4, plus four bleach shades BL1–BL4. Pre-shaded, ready to mill.
Shade colours on screen are indicative only.
A
A1
A2
A3
A3.5
A4
B
B1
B2
B3
B4
C
C1
C2
C3
C4
D
D2
D3
D4
BL
BL1
BL2
BL3
BL4
Specifications
The essentials.
Disc diameter
Ø 98.5 · 95 mm
Thickness
10 – 30 mm
Density
6.07 ± 0.03 g/cm³
Sintering temperature
1500 °C
Certifications
ISO 13485 · CE 1639 · FDA
Manufacturer
Shenzhen Yurucheng Dental Materials Co., Ltd.