43%
translucency
≥1100
MPa bending strength (avg.)
1200
HV hardness
1530 °C
recommended sintering
Why ST COLOR
The shade, consistent from disc to disc.
ST COLOR is pre-shaded in the mass: the same uniform colour through the whole disc, so every restoration comes out in the expected shade, with no infiltration or drying step.
Uniform colour
One consistent shade through the full thickness of the disc, for predictable results.
No post-dyeing
No coloring liquid, no immersion, no drying: one less step and fewer variables in the lab.
Full contour, multi-unit bridges
Full-contour crowns, anterior restorations and multi-unit bridges (max. 2 pontics between abutments).
Physical characteristics
| Sintered density | 6.07 ± 0.03 g/cm³ |
|---|---|
| Bending strength | ≥1100 MPa (avg.) |
| Transmittance | 43% |
| Hardness | 1200 HV |
| Yttria | 3Y |
| Sintering temperature | 1530 °C (recommended) |
Indications
From inlay to multi-unit bridge.
Crown
Inlay
Onlay
Multi-unit bridges (max. 2 pontics between abutments)
Anterior
Shade range
20 shades.
The full VITA classical range A1–D4, plus four bleach shades BL1–BL4. Pre-shaded, ready to mill.
Shade colours on screen are indicative only.
A
A1
A2
A3
A3.5
A4
B
B1
B2
B3
B4
C
C1
C2
C3
C4
D
D2
D3
D4
BL
BL1
BL2
BL3
BL4
Specifications
The essentials.
Disc diameter
Ø 98.5 · 95 mm
Thickness
10 – 30 mm
Density
6.07 ± 0.03 g/cm³
Sintering temperature
1530 °C
Certifications
ISO 13485 · CE 1639 · FDA
Manufacturer
Shenzhen Yurucheng Dental Materials Co., Ltd.