46%
translucency
≥900
MPa bending strength (avg.)
1200
HV hardness
1500 °C
recommended sintering
Why SHT ML
The shade is already in the disc.
With SHT ML the colour gradient is built into the zirconia. No infiltration step, no drying time: you go straight from milling to sintering.
5 layers, 9-shade gradient
Five stacked layers carry a 9-step colour gradient from cervical to incisal, already in the disc.
No further dyeing
No coloring liquid, no immersion, no drying: one less step and fewer variables in the lab.
Anterior to multi-unit bridges
Translucent enough for the anterior, strong enough for multi-unit bridges (max. 2 pontics between abutments).
Physical characteristics
| Sintered density | 6.07 ± 0.03 g/cm³ |
|---|---|
| Bending strength | ≥900 MPa (avg.) |
| Transmittance | 46% |
| Hardness | 1200 HV |
| Sintering temperature | 1500 °C (recommended) |
Layer by layer
5 layers · 9-step colour gradient
IncisalCervical
| Layer | Thickness | Translucency | Yttria | Strength |
|---|---|---|---|---|
| Layer 1 | 25% | 46% | 4Y | ≥900 MPa |
| Layer 2 | 15% | 46% | 4Y | ≥900 MPa |
| Layer 3 | 15% | 46% | 4Y | ≥900 MPa |
| Layer 4 | 15% | 46% | 4Y | ≥900 MPa |
| Layer 5 | 30% | 46% | 4Y | ≥900 MPa |
Indications
From inlay to bridge.
Crown
Inlay
Onlay
Multi-unit bridges (max. 2 pontics between abutments)
Anterior
Shade range
20 shades.
The full VITA classical range A1–D4, plus four bleach shades BL1–BL4. Pre-shaded, ready to mill.
Shade colours on screen are indicative only.
A
A1
A2
A3
A3.5
A4
B
B1
B2
B3
B4
C
C1
C2
C3
C4
D
D2
D3
D4
BL
BL1
BL2
BL3
BL4
Specifications
The essentials.
Disc diameter
Ø 98.5 · 95 mm
Thickness
10 – 30 mm
Density
6.07 ± 0.03 g/cm³
Sintering temperature
1500 °C
Certifications
ISO 13485 · CE 1639 · FDA
Manufacturer
Shenzhen Yurucheng Dental Materials Co., Ltd.