≥1200
MPa bending strength (avg.)
40%
translucency
1200
HV hardness
1530 °C
recommended sintering
Why HT PLUS
Strength and value, without compromise.
HT PLUS is the workhorse of the range: a white disc you shade to your own protocol, with the strength for frameworks and a price that keeps every case profitable.
High translucency
Around 40% translucency, for natural-looking results once shaded and finished.
≥1200 MPa, economical
Brilliant bending strength at the most accessible price in the range.
Copings & frameworks
The reliable base for layered restorations, crowns and bridges.
Physical characteristics
| Sintered density | 6.07 ± 0.03 g/cm³ |
|---|---|
| Bending strength | ≥1200 MPa (avg.) |
| Transmittance | 40% |
| Hardness | 1200 HV |
| Yttria | 3Y |
| Sintering temperature | 1530 °C (recommended) |
Indications
From inlay to framework.
Crown
Inlay
Onlay
Bridges
Coping
Shade it your way
A white disc, your shade.
HT PLUS comes white, with no built-in gradient: you choose the shade with coloring liquids before sintering, or with stains after. Full control, case by case.
Specifications
The essentials.
Disc diameter
Ø 98.5 · 95 mm
Thickness
10 – 30 mm
Colour
White
Sintering temperature
1530 °C
Certifications
ISO 13485 · CE 1639 · FDA
Manufacturer
Shenzhen Yurucheng Dental Materials Co., Ltd.